Influence of Plasma Pretreated Wood on Wood Surface Wetting

  • Categories:Industry News
  • Author:plasma cleaning machine-surface treatment equipment-CRF plasma machine-Sing Fung Intelligent Manufacturing
  • Origin:
  • Time of issue:2021-02-05
  • Views:

(Summary description)The wettability of wood is an important interface characteristic to describe the difficulty and effect of wetting, diffusion and bonding on wood surface when some liquids (water, adhesives, oxidants and cross-linkers, etc.) contact wood. Plasma pretreatment is of great significance for wood interface and various modification treatment processes. As a kind of natural polymer, wood not only has the dual characteristics of biology and physical chemistry, but also as an anisotropic material with inhomogeneity, its surface structure and chemical composition affect the adhesion of wood, and then affect the overall strength, toughness, durability and other properties of wood. Experimental method: put the wood veneer on the lower tray of the plasma cleaning machine, put the tray in the reaction chamber, and close the chamber door. Then open the vacuum pump to vacuum, pump to the corresponding vacuum, open the gas required for plasma treatment, press the RF key for plasma treatment, according to the test set time after treatment, the sheet out, sealed with a sealing paper, to be determined. Because of the aging of plasma treatment, the surface contact Angle of the treated samples should be tested in the shortest possible time. Results and analysis: By the plasma cleaning machine after pretreatment, about 3 minutes after the contact Angle is 113.8 ° dropped to about 50 °, with the extension of processing time, the contact Angle change tends to be stable or increase slightly, especially when the processing time is more than 7 min, wood surface by high energy electron, ion relatively uninterrupted, energy accumulation is bigger, the local have excessive corrosion phenomena, and plasma processing make the wood surface produces a large number of oxygen containing functional group and peroxide, including parts of the carboxyl and carbonyl hair base, lead to an increase in temperature of the wood in the plasma of high energy discharge, easy to cause local color darker wood surface, produce coking phenomenon. Therefore, low temperature plasma discharge treatment of wood, the treatment time of 3min is appropriate.

Influence of Plasma Pretreated Wood on Wood Surface Wetting

(Summary description)The wettability of wood is an important interface characteristic to describe the difficulty and effect of wetting, diffusion and bonding on wood surface when some liquids (water, adhesives, oxidants and cross-linkers, etc.) contact wood. Plasma pretreatment is of great significance for wood interface and various modification treatment processes.



As a kind of natural polymer, wood not only has the dual characteristics of biology and physical chemistry, but also as an anisotropic material with inhomogeneity, its surface structure and chemical composition affect the adhesion of wood, and then affect the overall strength, toughness, durability and other properties of wood.

Experimental method: put the wood veneer on the lower tray of the plasma cleaning machine, put the tray in the reaction chamber, and close the chamber door. Then open the vacuum pump to vacuum, pump to the corresponding vacuum, open the gas required for plasma treatment, press the RF key for plasma treatment, according to the test set time after treatment, the sheet out, sealed with a sealing paper, to be determined. Because of the aging of plasma treatment, the surface contact Angle of the treated samples should be tested in the shortest possible time.

Results and analysis: By the plasma cleaning machine after pretreatment, about 3 minutes after the contact Angle is 113.8 ° dropped to about 50 °, with the extension of processing time, the contact Angle change tends to be stable or increase slightly, especially when the processing time is more than 7 min, wood surface by high energy electron, ion relatively uninterrupted, energy accumulation is bigger, the local have excessive corrosion phenomena, and plasma processing make the wood surface produces a large number of oxygen containing functional group and peroxide, including parts of the carboxyl and carbonyl hair base, lead to an increase in temperature of the wood in the plasma of high energy discharge, easy to cause local color darker wood surface, produce coking phenomenon. Therefore, low temperature plasma discharge treatment of wood, the treatment time of 3min is appropriate.

  • Categories:Industry News
  • Author:plasma cleaning machine-surface treatment equipment-CRF plasma machine-Sing Fung Intelligent Manufacturing
  • Origin:
  • Time of issue:2021-02-05 10:01
  • Views:
Information

Influence of Plasma Pretreated Wood on Wood Surface Wetting:

The wettability of wood is an important interface characteristic to describe the difficulty and effect of wetting, diffusion and bonding on wood surface when some liquids (water, adhesives, oxidants and cross-linkers, etc.) contact wood. Plasma pretreatment is of great significance for wood interface and various modification treatment processes.

Plasma Pretreated Wood on Wood Surface Wetting

As a kind of natural polymer, wood not only has the dual characteristics of biology and physical chemistry, but also as an anisotropic material with inhomogeneity, its surface structure and chemical composition affect the adhesion of wood, and then affect the overall strength, toughness, durability and other properties of wood.

Experimental method: put the wood veneer on the lower tray of the plasma cleaning machine, put the tray in the reaction chamber, and close the chamber door. Then open the vacuum pump to vacuum, pump to the corresponding vacuum, open the gas required for plasma treatment, press the RF key for plasma treatment, according to the test set time after treatment, the sheet out, sealed with a sealing paper, to be determined. Because of the aging of plasma treatment, the surface contact Angle of the treated samples should be tested in the shortest possible time.

Results and analysis: By the plasma cleaning machine after pretreatment, about 3 minutes after the contact Angle is 113.8 ° dropped to about 50 °, with the extension of processing time, the contact Angle change tends to be stable or increase slightly, especially when the processing time is more than 7 min, wood surface by high energy electron, ion relatively uninterrupted, energy accumulation is bigger, the local have excessive corrosion phenomena, and plasma processing make the wood surface produces a large number of oxygen containing functional group and peroxide, including parts of the carboxyl and carbonyl hair base, lead to an increase in temperature of the wood in the plasma of high energy discharge, easy to cause local color darker wood surface, produce coking phenomenon. Therefore, low temperature plasma discharge treatment of wood, the treatment time of 3min is appropriate.

Scan the QR code to read on your phone

Relevant Information

Shenzhen Sing Fung Intelligent  Manufacturing Co., Ltd.

Adhere to quality as the foundation, honesty as the way of business, innovation as the source of development, and service as the pinnacle of value

©Shenzhen Sing Fung Intelligent Manufacturing Co., Ltd. All rights reserved
粤ICP备19006998号
dh

TEL:0755-3367 3020 / 0755-3367 3019

dh

E-mail:sales-sfi@sfi-crf.com

dh

ADD:Mabao Industrial Zone, Huangpu, Baoan District, Shenzhen